This study investigates the current-carrying tribological properties and wear mechanisms of copper–graphite composites under varying contact loads. Two copper– graphite composites with different graphite content were prepared using the pressure sintering method. Current-carrying tribological tests were conducted at three distinct contact loads. Scanning electron microscopy, X-ray diffraction, laser confocal microscopy, and pin-on-disk tribological testing were utilized to examine the current-carrying tribological properties and the worn morphologies of the materials. The results indicate that, under the three contact loads, the friction coefficient of the copper–graphite materials ranged from 0.3 to 0.5, the wear rate was on the order of 10−13 m3/(N·m), the average voltage drop varied between 0.7 and 1.6 V, and the average electrical noise ranged from 0.2 to 0.9 mV. The wear mechanism included delamination wear and a minor amount of abrasive wear, and the lubricating film formed on the surface was mainly composed of C, PbO, and CuO. Notably, copper–graphite composites with lower graphite content exhibited superior hardness, electrical conductivity, and relative density compared to those with higher graphite content. At a contact load of 0.31 N, the copper–graphite composite containing 30wt% graphite demonstrated the most favorable current-carrying tribological performance, characterized by the lowest wear rate (1.09 × 10−13 m3/(N·m)), voltage drop (0.943 V), and electrical noise (0.234 mV).
Loading....